Hostacom X M2 U36
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9sMGa0_Hostacom-X-M2-U36.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Hostacom" X M2 U36 is a 20% mineral filled PP copolymer with good stiffness toughness balance, low odour and fogging. Used typically for automotive interior, in particular for instrument panels. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.90 to 1.1 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 2500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus - Secant | 2500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | |
| 0°C | 3.5 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -35°C | 35 | kJ/m² | |
| -30°C | 35 | kJ/m² | |
| 23°C | 95 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/A50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging - 16h (100°C) | 6.0E-4 | g | DIN 75201B |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Emission 1(120°C) | 17.0 | µg/g | |
| Odor Rating 2(80°C) | 3 |
| Note Message | |
|---|---|
| 1 . | C Emission, PV 3341 (VW-Norm), 5h |
| 2 . | PV 3200 (VW-Norm), 2h, Note 1-6 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GFX1624-BK(PTFE) | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| TOTAL Polyethylene XSene® HDPE XS 10H | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| EVERLON® TZ-65 | Ever Polymer Co., Ltd. | SEBS+SBS | EVERLON® |
| KumhoSunny PC 202 | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| PLEXIGLAS® Sheet Optical RP Control 7D009 | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |