LNP™ STAT-KON™ KE002 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9rwglq_LNPSTATKONKE002compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON KE002 is a compound based on Acetal resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound KC-1002 Product reorder name: KE002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.0 - 3.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8220 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 1 | 106 | MPa | ASTM D638 |
| Fracture | 104 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 2 | 2.4 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 3 | 7.00 | MPa | ASTM D790 |
| -- 4 | 7050 | MPa | ISO 178 |
| Flexural Stress | 154 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 5 | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 370 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed, 64.0 mm Span) | 161 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+5 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 NG GF 20 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Monprene® CP-32060G TR BLK 8131 | Teknor Apex Company | TPE | Monprene® |
| LNP™ THERMOCOMP™ PX87791 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| Petrothene® NA960083 | LyondellBasell Industries | LDPE | Petrothene® |
| Hifax TYC 337P 3 S81466 | LyondellBasell Industries | PP Copolymer | Hifax |