STRATOR® C-6
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | EPIC Polymers |
| Trademark: | Strator® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9qaPaV_STRATOR-C-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STRATOR®C- 6 is a thermoplastic product that contains 60% long glass fibers as filler. It is available in Europe. The main characteristics are: high strength. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.72 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 22000 | 19000 | MPa | ISO 527-2 |
| 90°C | 14000 | -- | MPa | ISO 527-2 |
| 120°C | 13000 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 290 | 230 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 19000 | 15000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 450 | 350 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 38 | 40 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 92 | 100 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 238 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 1.8E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.35 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | ASTM D257 |
| Dielectric Strength (2.00 mm) | 36 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Additional Information |
|---|
| 干燥 The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 270 - 300 | °C | |
| Middle Temperature | 270 - 300 | °C | |
| Front Temperature | 285 - 310 | °C | |
| Nozzle Temperature | 285 - 320 | °C | |
| Processing (Melt) Temp | < 310 | °C | |
| Mold Temperature | 80.0 - 160 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 1088 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Sunny® PA6 EN400 | Guangdong Shunde Shunyan New Material Co., Ltd. | Nylon 6 | Sunny® |
| VESTOSINT® 1121 colored | Evonik Industries AG | Nylon 12 | VESTOSINT® |
| Elastron® V V601.A90.N | Elastron USA, Inc. | TPV | Elastron® V |
| Plaskon 7060 | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |