ACCULOY™ PCA083L
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCULOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9pUiC8_ACCULOY-PCA083L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCULOY™ PCA083L is a Polycarbonate + ABS (PC+ABS) product. It is available in North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/3.8 kg | 5.0 | g/10 min | |
| 250°C/5.0 kg | 17 | g/10 min | |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 53.0 | MPa | |
| Break | 42.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | |
| Break | 33 | % | |
| Flexural Modulus | 2600 | MPa | ASTM D790 |
| Flexural Strength | 81.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 580 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 106 | °C | |
| 1.8 MPa, Unannealed | 87.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badaflex® TPE-S 75A 1205 2K S2 | Bada AG | SEBS | Badaflex® |
| Clariant Nylon 6 PA213G33 | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| Formolene® 6550A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Plaslube® ABS/PBT 1000 | Techmer Engineered Solutions | ABS+PBT | Plaslube® |
| TechnoMid PA6 S GK 30 | TechnoCompound GmbH | Nylon 6 | TechnoMid |