LEXAN™ LUX1832 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9oyTes_LEXAN-LUX1832-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MFR=3.0; Branched extrusion grade for LED applications, UV stabilized; available in diffuse colors |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 0.90 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2230 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 62.0 | MPa | |
| Break | 60.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 7.0 | % | |
| Break | 94 | % | |
| Flexural Modulus 4(50.0 mm Span) | 2370 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 101 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 130 | J/m | |
| 23°C | 810 | J/m | |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 64.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 141 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 127 | °C | |
| Vicat Softening Temperature | 145 | °C | ASTM D1525 6 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 6.6E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.7E-5 | cm/cm/°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 to 87.8 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Cylinder Zone 1 Temp. | 166 | °C | |
| Cylinder Zone 2 Temp. | 171 | °C | |
| Cylinder Zone 3 Temp. | 177 | °C | |
| Cylinder Zone 4 Temp. | 182 | °C | |
| Melt Temperature | 182 to 199 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV X5780B | Teknor Apex Company | TPV | Sarlink® TPV |
| Sarlink® TPE ML-1180B BLK X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| Unipren® Elastomers A3 PRTA010 45A EG06S1 UP326 | Petropol Industry and Trade of Polymers LTDA | TPE | Unipren® Elastomers |
| Epoxies, Ect. 20-3068 (CAT.1) | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Karina IVORY PVC COMPOUND 105950-35/1-BY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |