INNOPOL® PP CS 2-2513 MF
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9nianH_INNOPOL-PP-CS-2-2513-MF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 2-2513 MF is a mineral, micro-fibre filled, elastomer modified compound based on polypropylene block-copolymer. This grade is available in nature and custom coloured form. Recommended application INNOPOL® CS 2-2513 MF is developed for producing injection moulded automotive interior components where the required properties are good stiffness and impact resistance besides excellent scratch resistance at a lower density. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 21.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.5 | kJ/m² | ISO 179/1eA |
| 23°C | 22 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 40 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 102 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 53.0 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 230 | °C | |
| Middle Temperature | 190 - 230 | °C | |
| Front Temperature | 190 - 230 | °C | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold pressure: 30 to 100 % of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS PPE-AG10 | Polymer Technology and Services, LLC | Nylon+PPE | PTS |
| Aurora PVC AP1000 Series | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| Edgetek™ ET3200-8093 FR Black | PolyOne Corporation | PC | Edgetek™ |
| POLYfill PPH T2020 | Polykemi AB | PP Homopolymer | POLYfill |
| Medalist® MD-12180 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Medalist™ |