LNP™ KONDUIT™ PX11311U compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ KONDUIT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9nZpnO_LNP-KONDUIT-PX11311U-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermally conductive mineral and glass fiber filled PA6 compliant with ECO protocols, non-brominated, non chlorinated |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.74 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 24 hr | 0.65 | % | |
| Flow : 24 hr | 0.45 | % | |
| Water Absorption (23°C, 24 hr) | 0.36 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 105 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 11000 | MPa | ISO 178 |
| Flexural Stress | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 209 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 208 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 185 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 205 | °C | ISO 306/B120 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass Pass | ||
| 165°C | Pass | ||
| CLTE | |||
| Flow : -40 to 40°C | 3.1E-5 3.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -30 to 80°C | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 80°C | 3.7E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.8E-5 4.8E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -30 to 80°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : 23 to 80°C | 7.3E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | ISO 22007-2 | ||
| -- 6 | 0.80 | W/m/K | |
| -- 7 | 1.1 1.1 | W/m/K | |
| -- 8 | 1.3 1.3 | W/m/K | |
| -- 9 | 1.5 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Dielectric Strength (1.60 mm, in Oil) | 16 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-0 | ||
| 1.00 mm, Testing by SABIC | V-0 V-0 | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 800 | °C | |
| 1.50 mm | 775 | °C | |
| 1.60 mm | 775 775 | °C | |
| 3.00 mm | 800 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 260 to 275 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 85.0 to 100 | °C | |
| Back Pressure | 0.200 to 0.300 | MPa | |
| Screw Speed | 20 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| 6 . | through-plane, 60*60*3mm plaque |
| 7 . | through-plane, ø80*3mm discs |
| 8 . | in-plane, ø80*3mm discs |
| 9 . | in-plane, 60*60*3mm plaque |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LHG284 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Nilac MT | Soredi S.p.a. | ABS | Nilac |
| Nypol® PA A3 G20 HS PRTA011 NR446 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Clyrell RC221M | LyondellBasell Industries | PP, Unspecified | Clyrell |
| Wuxi Jiahong EB-207X | Wuxi Jiahong Plastics Technology CO., Ltd. | PVC, Unspecified | Wuxi Jiahong |