TOTAL Polyethylene HDPE 6420
| Category: | HDPE, MMW , High Density (MMW) Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9nLDrf_TOTAL-Polyethylene-HDPE-6420.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Polyethylene 6420 is a high density (MMW) polyethylene material,. This product is available in North America or Asia Pacific region. The processing method is: film extrusion. The main features of TOTAL Polyethylene 6420 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.962 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 2.0 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 55 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus 1 | ASTM D882A | ||
| 1% secant, MD : 25 µm, blown film | 862 | MPa | ASTM D882A |
| 2% secant, MD : 25 µm, blown film | 689 | MPa | ASTM D882A |
| 1% secant, TD : 25 µm, blown film | 883 | MPa | ASTM D882A |
| 2% secant, TD : 25 µm, blown film | 703 | MPa | ASTM D882A |
| Tensile Strength 2 | ASTM D882A | ||
| MD : Yield, 25 µm, blown film | 26.2 | MPa | ASTM D882A |
| TD : Yield, 25 µm, blown film | 27.6 | MPa | ASTM D882A |
| MD : Broken, 25 µm, blown film | 51.7 | MPa | ASTM D882A |
| TD : Broken, 25 µm, blown film | 23.4 | MPa | ASTM D882A |
| Tensile Elongation 3 | ASTM D882A | ||
| MD : Broken, 25 µm, blown film | 700 | % | ASTM D882A |
| TD : Broken, 25 µm, blown film | 700 | % | ASTM D882A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 24 | g | ASTM D1922 |
| MD : 51 µm, Coextruded Film 4 | 70 | g | ASTM D1922 |
| TD : 25 µm, blown film | 390 | g | ASTM D1922 |
| TD : 51 µm, Coextruded Film 5 | 500 | g | ASTM D1922 |
| Water Vapor Transmission Rate | ASTM F1249 | ||
| 38°C, 25 µm, blown film | 3.9 | g/m²/24 hr | ASTM F1249 |
| 38°C, 51 µm, Coextruded Film 6 | 2.9 | g/m²/24 hr | ASTM F1249 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 199 - 210 | °C |
| Extrusion instructions |
|---|
| Recommended BUR: 2.0 to 3.5Recommended FLH/D: 4.0 to 6.0 |
| Note Message | |
|---|---|
| 1 . | 25 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | A/B/B 25/50/25% layer distribution LDPE/6420/6420, 2.5 BUR |
| 5 . | A/B/B 25/50/25% layer distribution LDPE/6420/6420, 2.5 BUR |
| 6 . | A/B/B 25/50/25% layer distribution LDPE/6420/6420, 2.5 BUR |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCOM® PC 740/4 UV CC1322-08LG | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| ALCOM® PA66 910/1 GF15 PTFE10 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| CP PRYME® Polyethylene PE100LLD-20M | Chase Plastics Services Inc. | LLDPE | CP PRYME® Polyethylene |
| Hostacom M1 U01 102942 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| CP PRYME® Nylon 6 N300HSL | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |