MAJORIS G400
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9mqEcC_MAJORIS-G400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS G400 is a special long glass fibre reinforced polypropylene grade, for injection moulding and extrusion. The long glass fibres, chemically coupled to the polypropylene matrix, are providing with outstanding mechanical properties. MAJORIS G400 is the natural version and is available in black (MAJORIS G400-8229). Other colours can be provided on request. APPLICATIONS MAJORIS G400 is intended for injection moulding of highly demanding technical applications. The excellent properties of MAJORIS G400 make it suitable for:
MAJORIS G400 can, in many of these applications, substitute other engineering plastics or metal alloys. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9430 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 152 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 7750 | MPa | ISO 178 |
| Flexural Stress 2 | 189 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 28 | kJ/m² | ISO 179/1eA |
| 23°C | 29 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 67 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 162 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 145 | °C | ISO 306/B |
| CLTE - Flow | ASTM D696 | ||
| -30°C | 4.4E-5 | cm/cm/°C | ASTM D696 |
| 23°C | 3.1E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 230 - 250 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 80.0 - 100 | °C | |
| Injection Pressure | 30.0 - 60.0 | MPa | |
| Injection Rate | Slow | ||
| Screw Speed | 30 - 150 | rpm | |
| Injection Velocity | 20 - 30 | mm/sec |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure.Back pressure: as low as possible, 0 to 10% |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALAT 9383GFR300 | AD majoris | PBT | MALAT |
| Synthos PS GP 585C | Synthos S.A. | PS (GPPS) | Synthos PS |
| ALCOM® PC 740/171 GY1127-05LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| Generic ABS+PC - Glass Fiber | Generic | PC+ABS | Generic |
| Karina COMP. PVC IVORY -E 75852-35/ 1-B-IS-A | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |