LNP™ STAT-KON™ Ultem_UC1200 compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9liCQ5_LNPSTATKONUltemUC1200compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-KON ULTEM_UC1200 compound is a 12% carbon fiber reinforced PEI. High modulus with ESD characteristics for high-heat applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 7.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.12 - 0.22 | % | Internal method |
| Transverse flow : 3.20mm | 0.30 - 0.50 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8140 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 131 | MPa | ASTM D638 |
| Fracture | 131 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 5.1 | % | ASTM D638 |
| Fracture | 5.1 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 100mm span 4 | 8270 | MPa | ASTM D790 |
| 50.0mm span 5 | 7830 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| Fracture, 50.0mm span 6 | 221 | MPa | ASTM D790 |
| Fracture, 100mm span 7 | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 420 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 6.21 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 213 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 209 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 210 | °C | ASTM D648 |
| Vicat Softening Temperature | 214 | °C | ASTM D1525 8 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 1.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : -20 to 150°C | 1.4E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 3.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -20 to 150°C | 4.0E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 4.0E+2 | ohms·cm | ASTM D257 |
| High Amp Arc Ignition (HAI) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 | |
| Static Decay 9 | 10 | msec | FTMS 101B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.57 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 360 - 404 | °C | |
| Middle Temperature | 371 - 421 | °C | |
| Front Temperature | 382 - 427 | °C | |
| Nozzle Temperature | 377 - 421 | °C | |
| Processing (Melt) Temp | 382 - 427 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.6 mm/min |
| 8 . | 标准 B (120°C/h), 载荷2 (50N) |
| 9 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600/508 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Unipren® Elastomers B3 PRTA010 65A UP316 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Epic Urethane S7475 | Epic Resins | PUR, Unspecified | Epic Urethane |
| LUVOCOM® 1301-8772/BK | Lehmann & Voss & Co. | PPS | LUVOCOM® |
| Plantic® HF301 | Plantic Technologies Limited | Biodeg Polymers | Plantic® |