Retpol® 1210 TF HS UV3
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9lGawB_Retpol-1210-TF-HS-UV3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CORTON 1210 TF HS UV3 is a 10% talc filled copolymer polypropylene compound. It is a medium to high flow injection moulding grade developed for rigid components requiring good impact strength. It is stabilized to meet automotive heat ageing and weathering requirements. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.2 to 1.6 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 80 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 74 | ||
| Shore D, 15 sec, 3.00 mm | 65 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 90 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 1690 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 61 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 1100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 116 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 57.0 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ULTEM™ HU2210 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| UMERIT® 1500F | UBE America, Inc. | LLDPE | UMERIT® |
| Karina WHITE PVC COMPOUND 752D10/152-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Ultramid® Structure A3WG8 LFX BK23215 | BASF Corporation | Nylon 66 | Ultramid® |
| Sylvin 4280-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |