AKROMID® B3 GK 30 black (1827)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9k7zW0_AKROMID-B3-GK-30-black-1827-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GK 30 black (1827) is a 30% glass bead filled polyamide 6 with low warpage and high surface appearance Applications are housings and covers in the automotive-, electro- and furniture industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.34 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 1.1 | -- | % | |
| Water Absorption (Saturation, 23°C) | 6.5 | -- | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 2.1 | -- | % | ISO 1110 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | ISO 2039-1 | |||
| H 358/30 | -- | 90.0 | MPa | |
| H 961/30 | 180 | -- | MPa |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4500 | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 75.0 | 40.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | > 3.5 | > 25 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 20 | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 185 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | -- | °C | ISO 306/B50 |
| Melting Temperature 1 | 222 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 10 K/min, DSC |
| 2 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V738A | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Maxelast® P1780 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Braskem PE LD 5000A | Braskem | LDPE | Braskem PE |
| E-RIALGLASS H 15 S 30 TG | RIALTI Srl | PP Homopolymer | E-RIALGLASS |
| Ketron® PEEK-HPV | Quadrant Engineering Plastic Products | PEEK | Ketron® |