| PA 6, non-reinforced,Extrusion, low viscosity, no additives |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.14 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 10 | -- | % | |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 140 | 50.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2800 | 800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 75.0 | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.0 | 25 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 20 | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2600 | 700 | MPa | ISO 178/A |
| Flexural Stress 2(3.5% Strain) | 90.0 | 20.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 3(23°C) | 5.0 | 8.0 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6,E, 14-030 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | < 5.0 | kJ/m² | |
| 23°C | 5.0 | 50 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | 55 kJ/m² | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 7.0 | 7.5 | kJ/m² | |
| 23°C | 7.0 | 50 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 150 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 40.0 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B120 |
| Melting Temperature 4 | 222 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+14 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 30 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 3.90 | 18.0 | ||
| 23°C, 1 MHz | 3.50 | 4.00 | ||
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Oxygen Index 5 | 24 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Pull Rate: 2 mm/min; 50% RH |
| 4 . | 10°C/min |
| 5 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 157V-4 LG | Teknor Apex Company | PVC, Flexible | APEX® |
| LNP™ LUBRICOMP™ NXCY620 compound | SABIC Innovative Plastics | PC+ABS | LNP™ LUBRICOMP™ |
| LUMISIL® LR 7600/70 A/B | Wacker Chemie AG | Silicone | LUMISIL® LR |
| Monprene® RG-17240 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| ULTEM™ CRS5111 resin | SABIC Innovative Plastics | PEI | ULTEM™ |