MAXAMID™ EPDM6G14-NC010
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Pier One Polymers, Inc. |
| Trademark: | MAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9iE5SU_MAXAMIDEPDM6G14NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MAXAMID™ EPD6G14 is also available in natural, internal and external lubricants, UV stabilized and other modifications. Further information and details are available upon request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 96.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 10 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3790 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 152 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.20 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® K307 | Chevron Phillips Chemical Company LLC | MDPE | Marlex® |
| Chemlon® 830GHI | Teknor Apex Company (Chem Polymer) | Nylon 6/12 | Chemlon® |
| HiFill FR® ABS FR UV BK | Techmer Engineered Solutions | ABS | HiFill FR® |
| Kepamid® 1345GF | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| Karina BLACK COLOR CONCENTRATE 48/ 1-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |