| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Pier One Polymers, Inc. |
| Trademark: | MAXATEL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9g4ptA_MAXATELACGC25ANAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MAXATEL®ACGC25A-NAT is a polyoxymethylene (POM) copolymer material, and its filler is 25% glass fiber reinforced material. This product is available in North America and is processed by injection molding. MAXATEL®The main characteristics of the ACGC25A-NAT are: copolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 5.0 - 7.0 | g/10 min | ASTM D1238 |
| Ash Content | 22 - 28 | % | ASTM D4218 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 103 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 5.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 7590 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 54 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 149 | °C | ASTM D648 |
| Peak Melting Temperature | 166 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 182 - 198 | °C | |
| Mold Temperature | 82 - 93 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil R7-3521-11 | NuSil Technology | Silicone | NuSil |
| Advanced Composites ADX-5001 | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| Hipolyene 8515 TY | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Jampilen HP564S | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| Osterlene® PPC30-SHINA | Osterman & Company | PP Impact Copolymer | Osterlene® |