Order Products : sales@su-jiao.com

UmaPET MHLIMH

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Ester Industries Ltd.
Trademark:	UmaPET
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	9f3eL7_UmaPET-MHLIMH.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

KEY FEATURES

UmaPET MHLIMH is high barrier matte metallized film, metallized on chemical surface other side plain. It exhibits high barrier properties along with superior metal to film bond strength/adhesion.

It has superior mechanical properties, flex crack resistance.

It shows silver finish from matte side as aluminiun foil appearance.

APPLICATIONS

UmaPET MHLIMH is used as high barrier layer in flexible packaging applications which require high barrier and high bond strength in laminates.

Used in flexible packaging for aluminium foil like appearance in laminates.

Typical usage as barrier layer in laminates for confectionary, snacks, instant drink powder, milk powder, tea, coffee etc.

General Information
Features	Barrier Resin Bondability Good Adhesion Good Crack Resistance High Gloss Metallizable
Uses	Film Laminates Packaging
Appearance	Matte Finish Silver
Forms	Film

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D1204
Flow : 150°C, 30 min, 0.0120 mm	2.5	%
Across Flow : 150°C, 30 min, 0.0120 mm	0.40	%
Surface Tension - Metallized side (12.0 µm)	56	mN/m	ASTM D2578

Films	Nominal Value	Unit	Test Method
Yield (12.0 µm)	59.5	m²/kg	Internal Method

Optical	Nominal Value	Unit	Test Method
Optical Density (12.0 µm)	-2.5 to 7.5	%	Internal Method

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	12	µm
Film Thickness - Recommended / Available	12 µm
Tensile Strength			ASTM D882
MD : Break, 12 µm	186	MPa
TD : Break, 12 µm	196	MPa
Tensile Elongation			ASTM D882
MD : Break, 12 µm	90	%
TD : Break, 12 µm	85	%
Oxygen Permeability ¹(23°C, 12 µm)	< 0.800	cm³/m²/24 hr	ASTM D3985
Water Vapor Transmission ²	< 0.60	g/m²/24 hr	ASTM F1249

Note Message
1 .	0%RH
2 .	37.8°C, 90%RH, 12 µm

Resin Grade	Manufacturer	Category	Trademark
Akulon® K224-HPG3	DSM Engineering Plastics	Nylon 6	Akulon®
Grilon® TSGL-50-4 nat	EMS-GRIVORY	Nylon 66/6	Grilon®
Lupoy® 3010-15	LG Chem Ltd.	PC	Lupoy®
PC-ABSCOM™ B300	Polymer Compounders Limited	PC+ABS	PC-ABSCOM™
TOTAL Polyethylene LDPE 1022 FN 24 (Injection)	TOTAL Refining & Chemicals	LDPE	TOTAL Polyethylene