Makrolon® Sheet AR
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® Sheet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9e2QPR_MakrolonSheetAR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Makrolon® AR sheet is a one or both sides hard-coated polycarbonate product that adds higher abrasion resistance and surface hardness to polycarbonate's inherent performance benefits of impact strength and clarity. The proprietary hard-coat also provides chemical resistance and long lasting outdoor weathering performance. This product is available in clear, a range of standard tints, or can be custom matched to any color. Makrolon AR sheet has a seven (7) year Limited Product Warranty against breakage, yellowing, and hazing. The terms of the warranty are available on request. Applications Flat architectural glazing, machine guards, and laminates |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 70 | ASTM D785 | |
| Class r | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2340 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 62.1 | MPa | ASTM D638 |
| Limit | 65.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 110 | % | ASTM D638 |
| Flexural Modulus | 2380 | MPa | ASTM D790 |
| Flexural Strength | 93.1 | MPa | ASTM D790 |
| Compressive Modulus | 2380 | MPa | ASTM D695 |
| Compressive Strength | 86.2 | MPa | ASTM D695 |
| Shear Modulus | 786 | MPa | ASTM D732 |
| Shear Strength | ASTM D732 | ||
| -- 1 | 68.9 | MPa | ASTM D732 |
| -- 2 | 41.4 | MPa | ASTM D732 |
| Poisson's Ratio | 0.38 | ASTM E132 | |
| Wear resistance- Delta Haze 3 | 2 | % | ASTM D1044 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shading Coefficient | NFRC 100-2010 | ||
| Clear : 5.99 mm | 0.970 | NFRC 100-2010 | |
| Gray or Bronze : 5.99 mm | 0.770 | NFRC 100-2010 | |
| U Factor | NFRC 100-2010 | ||
| Summer : 5.99 mm | 0.850 | BTU/hr/ft²/°F | NFRC 100-2010 |
| Summer : 9.53 mm | 0.780 | BTU/hr/ft²/°F | NFRC 100-2010 |
| Winter : 5.99 mm | 0.920 | BTU/hr/ft²/°F | NFRC 100-2010 |
| Winter : 9.53 mm | 0.850 | BTU/hr/ft²/°F | NFRC 100-2010 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flash Ignition Temperature | 440 | °C | ASTM D1929 |
| Horizontal Burn - AEB | cm | ASTM D635 | |
| Self Ignition Temperature | 550 | °C | ASTM D1929 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Chemical Resistance | Pass | ASTM D1308 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 850 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | No Break | ASTM D256 | |
| Instrumented Dart Impact (3.18 mm) | > 63.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 138 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 132 | °C | ASTM D648 |
| Brittleness Temperature | -129 | °C | ASTM D746 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.19 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 8.2E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.18 mm, in Air) | 15 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 10 Hz | 2.96 | ASTM D150 | |
| 60 Hz | 3.17 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 9.0E-4 | ASTM D150 | |
| Arc Resistance | ASTM D495 | ||
| -- 4 | 10.0 | sec | ASTM D495 |
| -- 5 | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | HB | UL 94 | |
| 10.0 mm | V-0 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542 | |
| Transmittance | ASTM D1003 | ||
| 3000 µm 6 | 86.0 | % | ASTM D1003 |
| 3000 µm 7 | 50.0 | % | ASTM D1003 |
| 3000 µm 8 | 50.0 | % | ASTM D1003 |
| 3000 µm 9 | 18.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Ultimate |
| 2 . | Yield |
| 3 . | 100 Cycles, CS-10F Wheel, 500 g load |
| 4 . | Steel Strip Electrode |
| 5 . | Tungsten Electrodes |
| 6 . | Clear |
| 7 . | I30 Gray |
| 8 . | K09 Bronze |
| 9 . | I35 Dark Gray |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP TPO TPO-277 P Black | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| Nypol® PA B3 G10 V20 PRTA011 NT354 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| KPOL-PP K-PPH 14.0 | KPOL Chem Co. | PP Homopolymer | KPOL-PP |
| Hylex® P1017 L1 HB | Entec Polymers | PC | Hylex® |
| LG ABS AF312A | LG Chem Ltd. | ABS | LG ABS |