POCAN® KU 1-7625 901510
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | LANXESS Asia/Pacific |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9cyiMC_POCAN-KU-1-7625-901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT+PC, 20 % glass fibers, injection molding, low tendency to warp, improved surface finish |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.39 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 30.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % | |
| Viscosity Number (Reduced Viscosity) | 62.0 | ml/g | ISO 1628 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.4 | % | ISO 527-2/5 |
| Flexural Modulus 1(23°C) | 5500 | MPa | ISO 178/A |
| Flexural Stress 2(23°C) | 140 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 3(23°C) | 3.5 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT+PC, GHMR, 09-050, GF20 | ISO 7792 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | < 10 | kJ/m² | |
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 35 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 115 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/B120 |
| Melting Temperature 4 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 4.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 7.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LH01019 - B | Premier Polymers, LLC. | LLDPE | Premier |
| PPR ABS01 | Premier Plastic Resins, Inc. | ABS | PPR |
| Geon™ Vinyl Rigid Extrusion 87560 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| EQUATE PE EFDA-7047 | EQUATE Petrochemical Company KSCC | LLDPE | EQUATE PE |
| KumhoSunny ABS 760 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |