Rilsan® M-AECV ORANGE TL
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9cf1ru_Rilsan-M-AECV-ORANGE-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| M- will be deleted after industrial qualification |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183/D |
| Melt Volume-Flow Rate (MVR) (235°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw D | 76 | ISO 868 | |
| Shaw D, 15 seconds | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 36.0 | MPa | ISO 527-2 |
| Fracture | 60.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | ISO 527-2 |
| Fracture | > 250 | % | ISO 527-2 |
| Flexural Modulus | 1060 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 77.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 51.0 | °C | ISO 75-2/A |
| Melting Temperature | 175 - 179 | °C | ISO 11357-3 |
| Additional Information |
|---|
| Test pieces conditioned in 15 days, 23°C - 50% R.H. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vikalloy P90 | Viking Polymers, LLC | PMMA+PVC | Vikalloy |
| HAIPLEN EP100 MF6 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| LNP™ THERMOCOMP™ DX06412H compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| TORZEN® G3000HSL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| TECHNYL® A 60G1 V25 BLACK 2N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |