Borlink™ LE0595
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borlink™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9cYdyw_Borlink-LE0595.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Borlink LE0595 is a crosslinkable black polyethylene compound, specially designed for semiconductive conductor screen and bonded insulation screen of energy cables. Borlink LE0595 is designed for semiconductive screens in XLPE medium and high voltage cables. It can be used as inner and outer screen for bonded cable construction and as inner screen for strippable cable constructions. Borlink LE0595 meets the applicable requirements as below when processed using sound extrusion practices and testing procedures
Borlink LE0595 is a ready-to-use semiconductive compound. It offers excellent thermal stability which provides robust cable extrusion and crosslinking at high surface temperature, allowing for high line speed. The excellent distribution of carbon black and additives in Borlink LE0595 results in a smooth semiconductive screen. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Moisture Content | 200 | ppm | Karl Fisher |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Properties - After Ageing 168 h (135°C) | < 20 | % | IEC 60811-401 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Set | IEC 60811-507 | ||
| Elongation under load, 0.20 MPa : 200°C | 25 | % | |
| Permanent deformation, 0.20 MPa : 200°C | 0.0 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Monsanto ODR | 61.0 | dNm | ASTM D2084 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 22.0 | MPa | ISO 527-2/25 |
| Tensile Strain (Break) | 200 | % | ISO 527-2/25 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ISO 3915 | ||
| 23°C | < 1.0E+2 | ohms·cm | |
| 90°C | < 1.0E+3 | ohms·cm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 4.0 | hr | |
| Melt Temperature | 120 to 135 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titalon® A030AS | Titan Plastics Compounds Co., Ltd. | ABS | Titalon® |
| Halene L 92001S | Haldia Petrochemicals Ltd. | LLDPE | Halene L |
| ESTACARB 1601 OPALE | Cossa Polimeri S.r.l. | PC | ESTACARB |
| DURACON® EX-09 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| SABIC® HDPE M40053S | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |