SABIC® LDPE HP0322N
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9bH8yS_SABIC-LDPE-HP0322N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description HP0322N is Low Density Polyethylene grade suitable for producing heavy duty films and contains no slip and antiblock additives. It gives outstanding toughness and optical properties in the film. Typical Applications HP0322N can be used for Heavy duty bags, industrial shrink films, construction and agricultural films. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 50 µm, blown film | 190 | MPa | ASTM D882 |
| 1% secant, TD : 50 µm, blown film | 220 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 31.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 450 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 690 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 200 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 400 | g | ASTM D1922 |
| TD : 50 µm, blown film | 300 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 11 | % | ASTM D1003 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.50 - 4.00 | ||
| Properties have been measured by producing 50 µ film with 2.5 BUR using 100% HP0322N. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 195 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoPrene 45A-1000 | KMI Group Inc. | TPV | PrimoPrene |
| Shin-Etsu Elastomer X-30-783U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Sylvin 8948-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Abstron HR60N | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Sylvin 9940-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |