Amilan® CM1001R
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9bBdnD_Amilan-CM1001R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Amilan® CM1001R is a Polyamide 6 (Nylon 6) product filled with 40% mineral. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.51 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow : 3.00 mm 1 | 0.80 to 1.0 | -- | % | |
| Flow : 3.00 mm 2 | 0.80 to 1.0 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.90 | -- | % | |
| Saturation, 23°C | 5.8 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | |||
| M-Scale, 23°C | 81 | -- | ||
| R-Scale, 23°C | 119 | -- | ||
| R-Scale, 80°C | 25 to 30 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 130 | -- | MPa | |
| 23°C | 95.0 | 55.0 | MPa | |
| 80°C | 40.0 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, -40°C | 2.0 | -- | % | |
| Break, 23°C | 2.5 | 2.5 | % | |
| Break, 80°C | 7.0 | -- | % | |
| Flexural Modulus | ISO 178 | |||
| -40°C | 6900 | -- | MPa | |
| 23°C | 5800 | 2300 | MPa | |
| 80°C | 1800 | -- | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 160 | -- | MPa | |
| 23°C | 145 | 70.0 | MPa | |
| 80°C | 60.0 | -- | MPa | |
| Shear Strength (23°C) | 73.0 | 62.0 | MPa | ASTM D732 |
| Taber Abrasion Resistance (1000 Cycles) | 0.400 | -- | mg | ISO 9352 |
| Coefficient of Friction - vs. Metal 3 | 0.150 | -- | Suzuki Method |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -40°C | 35 | -- | kJ/m² | |
| 23°C | 45 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 203 | -- | °C | ISO 75-2/B |
| Melting Temperature | 225 | -- | °C | DSC |
| CLTE - Flow | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 21 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant 4 | IEC 60250 | |||
| 23°C, 50 Hz | 4.60 | -- | ||
| 23°C, 1 kHz | 4.50 | -- | ||
| 23°C, 1 MHz | 3.80 | -- | ||
| Dissipation Factor 5 | IEC 60250 | |||
| 23°C, 50 Hz | 0.040 | -- | ||
| 23°C, 1 kHz | 0.030 | -- | ||
| 23°C, 1 MHz | 0.020 | -- | ||
| Arc Resistance 6 | 137 | -- | sec | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.794 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | Without Lubrication |
| 4 . | 60% RH |
| 5 . | 60% RH |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer N70M | Precision Polymer Engineering Ltd. | NBR | Precision Polymer |
| Sindustris PP R3401 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| SOLPLAST TH 9000B | UTEKSOL d.o.o. | SBS | SOLPLAST TH |
| Karina BLACK PVC COMPOUND 834-48/ 1-A-ERM-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Axiall PVC FG-9208 | Axiall Corporation | PVC, Rigid | Axiall PVC |