NEOFLON™ EP-7000

Category:	ETFE , Ethylene Tetrafluoroethylene Copolymer
Manufacturer:	DAIKIN AMERICA, INC.
Trademark:	NEOFLON™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	9b1Z7a_NEOFLON-EP-7000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
ETFE EP-7000 is a fluoropolymer specifically designed for the Automotive Industry. This resin has an excellent permeation resistance to hydrocarbons and adheres well to many kinds of plastics without adhesive or etching. ETFE EP-7000 can be easily co-extruded into multi layer tubing and offers the following advantages for automotive applications: Excellent permeation resistance to hydrocarbons Increased temperature resistance Excellent chemical resistance Co-extrusion with other resins (nylons, ETFE, EFEP) without adhesive or etching Cold impact resistance

Message

ETFE EP-7000 is a fluoropolymer specifically designed for the Automotive Industry. This resin has an excellent permeation resistance to hydrocarbons and adheres well to many kinds of plastics without adhesive or etching.

ETFE EP-7000 can be easily co-extruded into multi layer tubing and offers the following advantages for automotive applications:

Excellent permeation resistance to hydrocarbons

Increased temperature resistance

Excellent chemical resistance

Co-extrusion with other resins (nylons, ETFE, EFEP) without adhesive or etching

Cold impact resistance

General Information
Features	Good Adhesion Good Chemical Resistance High Heat Resistance Hydrocarbon Resistant Low Temperature Impact Resistance
Uses	Automotive Applications Tubing
Forms	Pellets
Processing Method	Coextrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.76	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (297°C/5.0 kg)	15 to 25	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	30.0 to 50.0	MPa	ASTM D3159
Tensile Elongation (Break)	370 to 530	%	ASTM D3159

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	255	°C	DSC

Additional Information	Nominal Value	Unit
Permeation Resistance - Average ¹(60°C)	2.5	g·mm/m²/atm/24 hr

Note Message
1 .	CE-10

Resin Grade	Manufacturer	Category	Trademark
KOPA® KN135G33BLHS	Kolon Plastics, Inc.	Nylon 6	KOPA®
Hyundai EP Barrier 180BYC/Natural	HYUNDAI EP Co., Ltd.	Polyolefin, Unspecified	Hyundai EP Barrier
LNP™ THERMOCOMP™ QF007 compound	SABIC Innovative Plastics	Nylon 610	LNP™ THERMOCOMP™
Sylvin 8376-92UV Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
NYLOY® CM-5000 8025B1	Nytex Composites Co., Ltd.	Nylon 6	NYLOY®