NORYL GTX™ APS130 resin
| Category: | PPS+PPE , Polyphenylene Sulfide + PPE |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9aP7Nz_NORYL-GTX-APS130-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPE+PPS GF30% |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 29 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.25 to 0.70 | % | Internal Method |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 113 | MPa | Internal Method |
| Tensile Elongation (Break) | 8.0 | % | Internal Method |
| Flexural Modulus | 8430 | MPa | ASTM D790 |
| Flexural Strength | 157 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 267 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 2.5E-5 to 5.5E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Dielectric Strength (1.60 mm, in Oil) | 22 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.30 | ||
| 60 Hz | 3.30 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 282 to 316 | °C | |
| Middle Temperature | 288 to 321 | °C | |
| Front Temperature | 293 to 327 | °C | |
| Nozzle Temperature | 299 to 332 | °C | |
| Processing (Melt) Temp | 299 to 332 | °C | |
| Mold Temperature | 93.3 to 149 | °C | |
| Back Pressure | 0.689 to 1.38 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7510 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Vydyne® 41 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Delta PCR-1G40 | Delta Polymers | PC | Delta |
| Infino NH-1021 | SAMSUNG SDI CO., LTD. | PC+ABS | Infino |
| XENOY™ 5220U resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |