Retpol® PDR 3039 HS UV3
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9Zp6IZ_Retpol-PDR-3039-HS-UV3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extron PDR 3039 HS UV3 is a 30% combined glass fibre and mineral reinforced coupled polypropylene compound. It is a medium flow injection moulding grade developed for components requiring high rigidity, high heat deflection temperatures, improved creep resistance, good dimensional stability and a better surface than achieved with straight glass filled compounds. It has been stabilized to meet automotive heat aging and exterior weathering requirements. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 109 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 81 | ||
| Shore D, 15 sec, 3.00 mm | 74 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 80.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 4580 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 76 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 157 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 147 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telene® 1810 A/B | Telene S.A.S., a Rimtec Corporation company | DCPD | Telene® |
| HOPELEX PCM-2303 | Lotte Chemical Corporation | PC | HOPELEX |
| Larpeek 10 K/40 | LATI S.p.A. | PEEK | Larpeek |
| INEOS PP 400-GA03 | INEOS Olefins & Polymers Europe | PP Impact Copolymer | INEOS PP |
| MACOMASS PP MM-PP HF 24 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |