EVALENE® HDPE HJ04602
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | JG Summit Petrochemical Corporation |
| Trademark: | EVALENE® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9YZWlC_EVALENEHDPEHJ04602.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EVALENE ® HJ04602 is a narrow molecular weight distribution resin intended to deliver robust performance for applications requiring toughness, balanced mechanical properties and good processability. EVALENE ® HJ04602 is designed to meet the rigorous processing requirements of high-speed injection and compression molding equipment, offering opportunities to achieve better economics without compromising performance. FEATURES
TYPICAL APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.960 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (48 hours) | 1.2 - 1.6 | % | Internal method |
| Environmental Stress-Cracking Resistance (10% Igepal, F50) | 4.00 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 1% Secant 2 | 1370 | MPa | ASTM D638 |
| Tensile Strength 3 | ASTM D638 | ||
| Yield | 26.0 | MPa | ASTM D638 |
| Fracture | 11.0 | MPa | ASTM D638 |
| Tensile Elongation 4 | ASTM D638 | ||
| Yield | 17 | % | ASTM D638 |
| Fracture | 1200 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 5 | 780 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6(23°C) | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 78.0 | °C | ASTM D648 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Temperature | 150 - 190 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 20 - 40 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 5.0 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Partial Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yuyao PBT 3055G20 | Yuyao Tenglong Plastics Co., Ltd. | PBT | Yuyao PBT |
| CYCOLAC™ MG38U resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| KRATON® G4610 H | Kraton Polymers LLC | SEBS | KRATON® |
| Hysol® EA9460 | Loctite® | Epoxy | Hysol® |
| Panlite® ML-7500ZCL | TEIJIN LIMITED | PC | Panlite® |