| 30% Glass Reinforced Polyethylene Terephthalate with Excellent High Temperature Dielectric Properties |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.60 | % | ISO 294-4 |
| Flow | 0.10 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 170 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 252 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 38 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.20 | IEC 60250 | |
| 1 MHz | 3.90 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.4E-3 | IEC 60250 | |
| 1 MHz | 0.015 | IEC 60250 | |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | mm/min | ISO 3795 |
| Flame Rating (0.9 mm) | HB | UL 94, IEC 60695-11-10, -20 | |
| FMVSS Flammability | B | FMVSS 302 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Specific Heat Capacity of Melt | 1500 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.29 | W/m/K |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 285 | °C | |
| Mold Temperature, Optimum | 140 | °C | |
| Back Pressure | As low as possible | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm | |
| Maximum Screw Tangential Speed | 200 | mm/sec |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.36 | g/cm³ | |
| Ejection Temperature | 170 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time - Desiccant Dryer | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 120 - 140 | °C | |
| Holding Pressure | 80.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL TP-G20 | Polymer Resources Ltd. | PBT | PRL |
| Sylvin 8301-90LG Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| AMTOPP BFP15 | Inteplast Group | PP, Unspecified | AMTOPP |
| Gallonprene® GP410-9501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| EPT 3062E | Mitsui Chemicals, Inc. | EPDM | EPT |