TOTAL Polystyrene Compound 827
| Category: | PS (IRPS) , Ignition Resistant Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9XiI1V_TOTAL-Polystyrene-Compound-827.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYSTYRENE CPDS 827 is a antimony trioxide and DBDPE free flame retardant, high impact polystyrene, suitable for hot glow wire test at 750°C. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 90.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Water Absorption, ISO 62: <0.1%Maxiumum Melt Temperature: 220°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravathane R210D52UV | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyether | Ravathane |
| SLOVAMID® 6 GF 10 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| STRANOX PP-ST40%LFT | Oxford Polymers | PP, Unspecified | STRANOX |
| Cellophane™ OptiTwist™ | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| LG PMMA IG840 | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |