Tecomid® NB30 GR15 BK005 FS90
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurotec Engineering Plastics |
| Trademark: | Tecomid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9XYRFc_Tecomid-NB30-GR15-BK005-FS90.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA6, 15% glass fiber reinforced, flame retardant - halogen & red phosphorus free, low smoke & toxic gas grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.67 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.70 | % | Internal method |
| Flow direction | 0.30 | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.1 | % | ISO 62 |
| Moisture Content | % | ISO 960 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Back Pressure | Low |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 35 | kJ/m² | ISO 180/1U |
| 23°C | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 205 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 185 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B |
| Melting Temperature 1 | 223 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 850 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 40.0 - 90.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 50.0 - 100 | MPa |
| Injection instructions |
|---|
| Pre-drying is not necessary for materials in moisture proof closed bags. |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Modified Plastics MN 6/6-FG 40 | Modified Plastics, Inc. | Nylon 66 | Modified Plastics |
| Braskem PP RP 250 | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| LIHAN® T9000EP | Nanjing Lihan Chemical Co., Ltd. | PBT | LIHAN® |
| Karina IVORY PVC COMPOUND 800-35/ 2-BR-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Panlite® AM-8030 | TEIJIN LIMITED | PC+Polyester | Panlite® |