Halene L 71602W
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene L |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9XSlPf_Halene-L-71602W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
71602W is a LLDPE film grade produced by Spherilene Technology. 71602W is without Slip additives and Antiblock and can be used in Packaging Film Applications. The precise morphological control achieved during polymerization confers good processability and mechanical strengths. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.916 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 12.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 11.0 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 23.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 19.0 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 500 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 750 | % | ASTM D882 |
| Dart Drop Impact 4(25 µm, Blown Film) | 50 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 60 | g | ASTM D1922 |
| TD : 25 µm, blown film | 280 | g | ASTM D1922 |
| Additional Information |
|---|
| Die gap: 2.5 mmBUR: 2.5 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 - 200 | °C | |
| Cylinder Zone 2 Temp. | 170 - 200 | °C | |
| Cylinder Zone 3 Temp. | 170 - 200 | °C | |
| Cylinder Zone 4 Temp. | 170 - 200 | °C | |
| Cylinder Zone 5 Temp. | 170 - 200 | °C | |
| Melt Temperature | 190 - 200 | °C |
| Extrusion instructions |
|---|
| Blow up Ratio: 2.0 to 3.0Die Gap: 2.0 to 2.5 mm |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | 38 mm Dart, 66 cm Height |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 300 80A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| SPESIN® KP213HIBL | Kolon Plastics, Inc. | PBT | SPESIN® |
| Network Polymers PP PPB 25 3502 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Chemical Resources BPP200 | Chemical Resources, Inc. | PP Impact Copolymer | Chemical Resources |
| ISOLOSS® LS-2000 | E-A-R Specialty Composites | PUR, Unspecified | ISOLOSS® |