MAJORIS G300
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9X7SYK_MAJORIS-G300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS G300 is a special long glass fibre reinforced polypropylene grade, for injection moulding and extrusion. The long glass fibres, chemically coupled to the polypropylene matrix, are providing with outstanding mechanical properties. MAJORIS G300 is available both in natural (MAJORIS G300) and black (MAJORIS G300 - 8229). Other colours can be provided on request. APPLICATIONS MAJORIS G300 is intended for injection moulding of highly demanding technical applications. The excellent properties of MAJORIS G300 make it suitable for:
MAJORIS G300 can, in many of these applications, substitute other engineering plastics or metal alloys. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Vertical flow direction | 0.55 | % | |
| Flow direction | 0.45 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 125 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2/50 |
| Flexural Modulus | 6500 | MPa | ISO 178 |
| Flexural Stress 1 | 151 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 26 | kJ/m² | ISO 179/1eA |
| 23°C | 23 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 57 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 160 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 145 | °C | ISO 306/B |
| CLTE - Flow | ASTM D696 | ||
| -30°C | 5.1E-5 | cm/cm/°C | ASTM D696 |
| 23°C | 4.1E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 230 - 250 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 80.0 - 100 | °C | |
| Injection Pressure | 30.0 - 60.0 | MPa | |
| Injection Rate | Slow | ||
| Screw Speed | 30 - 150 | rpm | |
| Injection Velocity | 20 - 30 | mm/sec |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressureBack pressure: as low as possible, 0 to 10% |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® SP-13168 | Teknor Apex Company | TPE | Monprene® |
| AMPLIFY™ TY 1053H | The Dow Chemical Company | MAH-g | AMPLIFY™ TY |
| Elastollan® 754 D HPM | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Petro Rabigh PP AV161 | Rabigh Refining & Petrochemical Co. | PP Impact Copolymer | Petro Rabigh PP |
| Sumiliteresin® PR-2217 I | SBHPP | Phenolic | Sumiliteresin® |