Order Products : sales@su-jiao.com
EMERGE™ PC 8731
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9WPgH2_EMERGE-PC-8731.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE PC 8731 Advanced Resin is an ignition-resistant, 10% glass reinforced, and UV resistant polycarbonate resin. EMERGE PC 8731 is rated as f1 resin by Underwriters Laboratory. This resin contains no bromine, chlorine, or phosphate additives. It is a medium flow PC resin with a mold release system, intended for injection molding applications. Applications
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 4000 | MPa | ASTM D638 |
| Tensile Strength (Break, 3.20 mm, Injection Molded) | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.20 mm, Injection Molded) | 4.0 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 3300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 141 | °C | |
| 1.8 MPa, Unannealed | 133 | °C | |
| 1.8 MPa, Annealed | 139 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 1 | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 290 to 315 | °C | |
| Mold Temperature | 80.0 to 115 | °C |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 802 SI 2 | RTP Company | Acetal (POM) Copolymer | RTP |
| Tisoplen® PPH 20 MNF CALCITE | Tisan | PP Homopolymer | Tisoplen® |
| Geon™ Vinyl Flexible P484B | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| KOPA® KN331F | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| PLUSTEK PA880 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |