Altuglas® MI-8E
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Altuglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9TSgwL_Altuglas-MI-8E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Altuglas® MI-8E is a Polymethyl Methacrylate Acrylic product. It is available in Asia Pacific or Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 0.70 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.20 to 0.80 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.34 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 56 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 35 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 72.5 | MPa | ISO 178 |
| Compressive Stress (23°C) | 64.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/2U |
| Notched Izod Impact Strength (23°C) | 4.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 101 | °C | ISO 306/B |
| CLTE - Flow (-30 to 23°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 3.85 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.040 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 1 | 1.490 | ISO 489 | |
| Transmittance | 91.0 | % | ASTM D1003 |
| Haze | 1.5 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 235 to 245 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razamid® A111 GR30 | Razin™ Engineering Plastics | Nylon 66 | Razamid® |
| UNITEM® PEI | Nytef Plastics, Ltd. | PEI | UNITEM® |
| Zytel® RS LC2800 NC010 | DuPont Performance Polymers | Nylon, Unspecified | Zytel® RS |
| Fainplast PVC FKA 89 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Hifax CA 1110 G2 | LyondellBasell Industries | PP Impact Copolymer | Hifax |