Petrothene® LP540200
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9SYCOm_Petrothene-LP540200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene LP540200 is a copolymer resin designed for blown film applications. This resin offers high ESCR, stiffness, excellent appearance and bubble stability. LP540200 is recommended for high strength multi-wall sack liners and barrier sheeting. It is also useful as a blend component for improved stiffness and machinability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.17 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F50) | > 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 21.9 | MPa | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 51 µm, blown film | 565 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm | 758 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm, blown film | 19.3 | MPa | ASTM D882 |
| TD : Yield, 51 µm, blown film | 22.8 | MPa | ASTM D882 |
| MD : Broken, 51 µm, blown film | 46.9 | MPa | ASTM D882 |
| TD : Broken, 51 µm, blown film | 29.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 510 | % | ASTM D882 |
| TD : Broken, 51 µm, blown film | 680 | % | ASTM D882 |
| Dart Drop Impact (51 µm, Blown Film) | 70 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm, blown film | 40 | g | ASTM D1922 |
| TD : 51 µm, blown film | 1200 | g | ASTM D1922 |
| Oxygen Permeability (51 µm, Blown Film) | 2450 | cm³/m²/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (51 µm, Blown Film) | 5.1 | g/m²/24 hr | ASTM F372 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 64.0 | °C | ASTM D648 |
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 119 | °C | ASTM D1525 |
| Additional Information |
|---|
| Film properties obtained from 2.0 mil Blown film, 2.5:1 Blow-up ratio, Melt Temperature 390 to 410°F, 60 mil die gap. |
| Note Message | |
|---|---|
| 1 . | Type 4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo Phenolic FM 4005X4648 | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| Wah Hong DAP WH-9100- BLK D | Wah Hong Industrial Corp. | DAP | Wah Hong DAP |
| 3M™ Dyneon™ Fluoroplastic THV 500GX4Z | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroplastic |
| Paracril OZO® 3341 | INSA | PVC+NBR | Paracril OZO® |
| Sylvin 4280-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |