Order Products : sales@su-jiao.com
Braskem PE SLH0820/30AF
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9RpXbV_Braskem-PE-SLH0820-30AF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SLH0820/30AF is a LLDPE hexene copolymer produced by Braskem. It offers outstanding processability combined with excellent mechanical properties. Very low gel amount. The minimum biobased content of this grade is 84%, determined according to ASTM D6866. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 50.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 40.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 950 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 1200 | % | ASTM D882 |
| Flexural Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm, Blown Film | 170 | MPa | ASTM D882 |
| 1% Secant, TD : 25 µm, Blown Film | 180 | MPa | ASTM D882 |
| Dart Drop Impact 1(25 µm, Blown Film) | 170 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 270 | g | ASTM D1922 |
| TD : 25 µm, blown film | 500 | g | ASTM D1922 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 84 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 210 | °C |
| Extrusion instructions |
|---|
| Blow up Ratio: from 2 to 3:1Die Gap: from 1.8 to 2.5 mmScreen Package(Mesh): 40/40 - 100% pure; 40/60/40 - blendMass temperature: 220°C (max 230°C) |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A RV300L 333 NER | Radici Plastics | Nylon 66 | Radilon® |
| TRIBOCOMP® PBT CF30 TS0 | EPIC Polymers | PBT | TRIBOCOMP® |
| NEFTEKHIM PP 1362S (HOXP2004) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| HIPOLEN P® TM 21 | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |
| Sylvin 9604-95 Blue 8441 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |