NORYL GTX™ GTX8120P resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9ReGOI_NORYL-GTX-GTX8120P-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GTX8120P is a glass filled extrudable NORYL GTX with low thermal conductivity, suitable for thermal breaks |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/10.0 kg) | 4.00 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 2.5 | % | |
| Equilibrium, 23°C, 50% RH | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6800 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 125 | MPa | |
| Break | 125 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 3.0 | % | |
| Break | 3.5 | % | |
| Flexural Modulus 1 | 5000 | MPa | ISO 178 |
| Flexural Stress | 175 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength 3 | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(0.45 MPa, Unannealed, 64.0 mm Span) | 240 | °C | ISO 75-2/Bf |
| Vicat Softening Temperature | 235 | °C | ISO 306/B50, ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.5E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 7.5E-5 | cm/cm/°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Melt Temperature | 270 to 280 | °C | |
| Calibration Temp, First | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 sp=62mm |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1680 BLK580 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TITANLENE® LDF 800GG | Lotte Chemical Titan (M) Sdn. Bhd. | LDPE | TITANLENE® |
| Amodel® A-1145 DW | Solvay Specialty Polymers | PPA | Amodel® |
| Keyflex® BT 3038D | LG Chem Ltd. | TPC-ET | Keyflex® BT |
| LNP™ THERMOCOMP™ WF007 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |