Generic LLDPE
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9RPbMw_Generic-LLDPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic LLDPE This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.905 - 0.932 | g/cm³ | ASTM D792 |
| 23°C | 0.900 - 0.931 | g/cm³ | ISO 1183 |
| -- | 0.910 - 0.940 | g/cm³ | ASTM D1505 |
| -- | 0.916 - 0.937 | g/cm³ | ASTM D4883 |
| Apparent Density | 0.13 - 0.56 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.10 - 4.0 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 0.20 - 6.3 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (23°C) | 0.317 - 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 49 - 62 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 244 - 422 | MPa | ASTM D638 |
| 23°C | 178 - 494 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 7.42 - 21.4 | MPa | ASTM D638 |
| Yield, 23°C | 7.69 - 17.3 | MPa | ISO 527-2 |
| Fracture, 23°C | 6.96 - 31.4 | MPa | ASTM D638 |
| Fracture, 23°C | 9.45 - 32.7 | MPa | ISO 527-2 |
| 23°C | 8.27 - 36.1 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.0 - 23 | % | ASTM D638 |
| Yield, 23°C | 14 - 22 | % | ISO 527-2 |
| Fracture, 23°C | 47 - 1000 | % | ASTM D638 |
| Fracture, 23°C | 290 - 940 | % | ISO 527-2 |
| Apparent Bending Modulus (23°C) | 260 - 271 | MPa | ASTM D747 |
| Flexural Modulus | |||
| 23°C | 209 - 771 | MPa | ASTM D790 |
| 23°C | 110 - 653 | MPa | ISO 178 |
| Flexural Strength | ASTM D790 | ||
| 23°C | 7.75 - 13.0 | MPa | ASTM D790 |
| Yield, 23°C | 176 - 281 | MPa | ASTM D790 |
| Coefficient of Friction | 0.086 - 0.52 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 24 - 54 | µm | |
| Film Puncture Energy | 4.44 | J | |
| Film Puncture Force | 30.7 - 62.8 | N | |
| Film Puncture Resistance | 14.6 | J/cm³ | |
| Film strength | ASTM D882 | ||
| MD | 209 | J/cm³ | ASTM D882 |
| TD | 222 | J/cm³ | ASTM D882 |
| secant modulus | |||
| MD | 108 - 230 | MPa | ASTM D882 |
| TD | 116 - 291 | MPa | ASTM D882 |
| 23°C | 90.0 - 272 | MPa | ISO 527-3 |
| Tensile Strength | |||
| MD : Yield | 7.98 - 13.2 | MPa | ASTM D882 |
| TD : Yield | 8.81 - 13.3 | MPa | ASTM D882 |
| Yield, 23°C | 5.20 - 16.9 | MPa | ISO 527-3 |
| MD : Fracture | 30.0 - 57.3 | MPa | ASTM D882 |
| TD : Fracture | 19.0 - 45.2 | MPa | ASTM D882 |
| Fracture, 23°C | 24.0 - 50.0 | MPa | ISO 527-3 |
| 23°C | 21.6 - 56.8 | MPa | ISO 527-3 |
| Tensile Elongation | |||
| MD : Yield | 12 - 530 | % | ASTM D882 |
| TD : Yield | 4.0 - 760 | % | ASTM D882 |
| MD : Fracture | 350 - 910 | % | ASTM D882 |
| TD : Fracture | 660 - 920 | % | ASTM D882 |
| Fracture, 23°C | 520 - 920 | % | ISO 527-3 |
| Flexural Modulus | ASTM D790 | ||
| MD | 180 | MPa | ASTM D790 |
| TD | 200 | MPa | ASTM D790 |
| Dart Drop Impact | |||
| 23°C | 45 - 210 | g | ASTM D1709 |
| 23°C | 35 - 270 | g | ISO 7765-1 |
| Elmendorf Tear Strength | |||
| MD | 0.0 - 490 | g | ASTM D1922 |
| TD | 8.0 - 810 | g | ASTM D1922 |
| -- | 1.8 - 6.0 | N | ISO 6383-2 |
| Seal Initiation Temperature | 99.4 - 130 | °C |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength (23°C) | 78.0 - 186 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 240 - 550 | J/m | ASTM D256 |
| 23°C | 23 - 50 | kJ/m² | ISO 180 |
| Multi-Axial Instrumented Impact Energy (23°C) | 15.0 - 63.0 | J | ISO 6603-2 |
| Tensile Impact Strength | |||
| 23°C | 56.7 - 1710 | kJ/m² | ASTM D1822 |
| 23°C | 265 | kJ/m² | ISO 8256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 41.9 - 74.1 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 34.0 - 70.9 | °C | ASTM D648 |
| Brittleness Temperature | |||
| -- | -76.4 - -69.0 | °C | ASTM D746 |
| -- | -70.4 - -70.0 | °C | ISO 974 |
| Vicat Softening Temperature | |||
| -- | 86.4 - 121 | °C | ASTM D1525 |
| -- | 92.0 - 118 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 119 - 126 | °C | |
| -- | 120 - 127 | °C | DSC |
| -- | 114 - 127 | °C | ISO 11357-3 |
| -- | 121 - 127 | °C | ASTM D3418 |
| -- | 119 - 127 | °C | ISO 3146 |
| Peak Crystallization Temperature (DSC) | |||
| -- | 103 - 127 | °C | ASTM D3418 |
| -- | 105 - 127 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+5 - 1.7E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 20 - 30 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 2.10 - 2.55 | ASTM D150 | |
| Dissipation Factor (23°C) | 1.0E-4 - 3.0E-3 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | 35 - 82 | ASTM D523 | |
| Gloss | 30 - 95 | ASTM D2457 | |
| Transmittance | 68.0 - 92.3 | % | ASTM D1003 |
| Clarity | 26.9 - 95.3 | ASTM D1746 | |
| Haze | 0.40 - 21 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 176 - 200 | °C | |
| Middle Temperature | 184 - 200 | °C | |
| Front Temperature | 184 - 205 | °C | |
| Nozzle Temperature | 204 - 205 | °C | |
| Processing (Melt) Temp | 180 - 285 | °C | |
| Mold Temperature | 17.5 - 30.0 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic LLDPEThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 185 - 188 | °C | |
| Cylinder Zone 1 Temp. | 159 - 201 | °C | |
| Cylinder Zone 2 Temp. | 178 - 196 | °C | |
| Cylinder Zone 3 Temp. | 178 - 250 | °C | |
| Cylinder Zone 4 Temp. | 177 - 261 | °C | |
| Cylinder Zone 5 Temp. | 179 - 236 | °C | |
| Adapter Temperature | 210 - 282 | °C | |
| Melt Temperature | 166 - 277 | °C | |
| Melt Temperature (Aim) | 190 | °C | |
| Die Temperature | 170 - 271 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic LLDPEThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® SXXIC BLUE | SRF Ltd. | Nylon 6 | TUFNYL® |
| ARMAMID® PA NE 30-3M | Poly Plastic | Nylon 6 | ARMAMID® |
| KOPA® KN133G50GR | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| PHOENIX™ 14501 | Phon Tech Industrial Company | TPE | PHOENIX™ |
| TechnoFiber PP LGF 30-10-01 HI | TechnoCompound GmbH | PP, Unspecified | TechnoFiber |