DENYL 66 4060
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Vamp Tech |
| Trademark: | DENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9RK2BP_DENYL-66-4060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 40% mineral filled, not Flame Retardant compound, good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.80 | % | |
| Across Flow | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 3.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 160 | °C | ASTM D648A |
| Vicat Softening Temperature | 235 | °C | ASTM D1525 1 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 100 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAKETON MV | A. Schulman Europe | PK-Aliphatic | SCHULAKETON |
| SUSTAMID 6G PD 120 | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| Tool-A-Thane UT-605 | Urethane Tooling & Engineering Corp | PUR, Unspecified | Tool-A-Thane |
| Unilex™ UP 9035-I | United Polychem | PP Impact Copolymer | Unilex™ |
| Axpoly® PP19 1033 | Axion Polymers | PP Homopolymer | Axpoly® |