Vistek 1862 U
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Visual Polymer Technologies, LLC |
| Trademark: | Vistek |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9P7Gmp_Vistek-1862-U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vistek 1862 U is a thermoplastic material,. This product is available in North America,. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 13 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 36.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 28 | % | ASTM D638 |
| Flexural Modulus | 1880 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 48.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 82.2 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 90.0 | % | ASTM D1003 |
| Haze | 4.3 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 193 - 232 | °C | |
| Middle Temperature | 193 - 232 | °C | |
| Front Temperature | 193 - 232 | °C | |
| Mold Temperature | 26.7 - 54.4 | °C |
| Injection instructions |
|---|
| Pre-drying is typically not needed. In excessive humidity, pre-dry at 160° F for 2 to 4 hours.Back Pressure: Medium to High |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 6202-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Unichem 105 | Colorite Polymers | PVC, Unspecified | Unichem |
| Axiall PVC 19482 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Karina WHITE PVC COMPOUND -E 753D10/ 11-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| S.O.E.™ S1611 | AKelastomers | SBC | S.O.E.™ |