Generic PEEK
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9Oeg3Y_Generic-PEEK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PEEK This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.29 - 1.37 | g/cm³ | ASTM D792 |
| 23°C | 1.29 - 1.32 | g/cm³ | ISO 1183 |
| Apparent Density | 0.30 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 1.6 - 36 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (380°C/10.0 kg) | 14.1 - 23.8 | cm³/10min | ISO 1133 |
| Spiral Flow | 10.0 - 30.0 | cm | |
| Molding Shrinkage | |||
| Flow : 23°C | 0.10 - 1.6 | % | ASTM D955 |
| Transverse flow : 23°C | 1.2 - 1.9 | % | ASTM D955 |
| 23°C | 1.2 - 1.3 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.049 - 0.21 | % | ASTM D570 |
| 23°C, 24 hr | 0.061 - 0.50 | % | ISO 62 |
| Saturated, 23°C | 0.30 - 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.049 - 0.40 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 96 - 106 | ASTM D785 | |
| Durometer Hardness (23°C) | 85 - 88 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2610 - 4770 | MPa | ASTM D638 |
| 23°C | 3350 - 4700 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 74.1 - 113 | MPa | ASTM D638 |
| Yield, 23°C | 72.1 - 113 | MPa | ISO 527-2 |
| Fracture, 23°C | 37.6 - 102 | MPa | ASTM D638 |
| Fracture, 23°C | 68.6 - 100 | MPa | ISO 527-2 |
| 23°C | 86.6 - 102 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 4.9 - 10 | % | ASTM D638 |
| Yield, 23°C | 4.9 - 5.1 | % | ISO 527-2 |
| Fracture, 23°C | 1.2 - 60 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 41 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2510 - 4660 | MPa | ASTM D790 |
| 23°C | 2500 - 4430 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 91.2 - 179 | MPa | ASTM D790 |
| 23°C | 104 - 179 | MPa | ISO 178 |
| Compressive Strength | |||
| 23°C | 116 - 155 | MPa | ASTM D695 |
| 23°C | 26.1 - 200 | MPa | ISO 604 |
| Shear Strength (23°C) | 52.4 - 95.1 | MPa | ASTM D732 |
| Poisson's Ratio (23°C) | 0.33 - 0.41 | ASTM E132 | |
| Coefficient of Friction | 0.080 - 0.53 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1600 - 2510 | MPa | ISO 527-3 |
| Tensile Stress (Break, 23°C) | 110 - 130 | MPa | ISO 527-3 |
| Tensile Elongation (Break, 23°C) | 150 - 200 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.9 - 8.2 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 23 - 92 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 50 - 98 | J/m | ASTM D256 |
| 23°C | 4.4 - 9.4 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 260 - 2200 | J/m | ASTM D256 |
| 23°C | 30 - 94 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 155 - 206 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 145 - 320 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 149 - 160 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 155 - 162 | °C | ASTM D648 |
| Continuous Use Temperature | 248 - 252 | °C | ASTM D794 |
| Glass Transition Temperature | |||
| -- | 143 | °C | ISO 11357-2 |
| -- | 143 - 150 | °C | DSC |
| Vicat Softening Temperature | 280 - 335 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 340 - 343 | °C | ISO 11357-3 |
| -- | 340 - 344 | °C | DSC |
| -- | 340 - 345 | °C | ASTM D3418 |
| Linear thermal expansion coefficient | |||
| Flow | 4.5E-5 - 4.8E-5 | cm/cm/°C | ASTM D696 |
| Flow | 4.3E-5 - 5.0E-5 | cm/cm/°C | ASTM E831 |
| Flow | 3.0E-5 - 6.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.9E-5 - 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | |||
| 23°C | 0.24 - 0.31 | W/m/K | ASTM C177 |
| 23°C | 0.25 - 0.29 | W/m/K | ISO 8302 |
| RTI Elec | 258 - 260 | °C | UL 746 |
| RTI Imp | 179 - 260 | °C | UL 746 |
| RTI | 240 - 260 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+2 - 1.9E+17 | ohms | ASTM D257 |
| -- | 1.0E+3 - 1.3E+14 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 2.0 - 1.9E+16 | ohms·cm | ASTM D257 |
| 23°C | 8.4E+14 - 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 7.5 - 21 | kV/mm | ASTM D149 |
| 23°C | 16 - 200 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 2.80 - 3.61 | ASTM D150 | |
| 23°C | 3.10 - 3.20 | IEC 60250 | |
| 23°C | 2.81 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 0.0 - 0.013 | ASTM D150 | |
| 23°C | 1.0E-3 - 5.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 149 - 200 | V | IEC 60112 |
| Insulation Resistance (23°C) | 9.8E+11 - 1.0E+12 | ohms | IEC 60167 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 24 - 35 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | 90.0 - 507 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 152 | °C | |
| Drying Time | 3.0 - 7.0 | hr | |
| Rear Temperature | 354 - 366 | °C | |
| Middle Temperature | 385 - 386 | °C | |
| Front Temperature | 374 - 395 | °C | |
| Nozzle Temperature | 370 - 371 | °C | |
| Processing (Melt) Temp | 373 - 391 | °C | |
| Mold Temperature | 179 - 191 | °C | |
| Injection Pressure | 101 - 104 | MPa | |
| Back Pressure | 0.500 - 0.553 | MPa | |
| Screw Speed | 55 - 80 | rpm | |
| Clamp Tonnage | 5.5 - 9.0 | kN/cm² |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PEEKThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 3.0 | hr |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PEEKThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 515A | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |
| Shinko-Lac® ABS TR-7 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| Wah Hong UP WH-8100-BLK FDA | Wah Hong Industrial Corp. | Polyester Alloy | Wah Hong UP |
| Anjatech® 250-T2/GF30 | Almaak International GmbH | Nylon 6 | Anjatech® |
| Larpeek 50 K/30 | LATI S.p.A. | PEEK | Larpeek |