EMERGE™ PC 4701-13
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9O9S4c_EMERGE-PC-4701-13.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC 4701-13 Advanced Resin is formulated with 10% glass fiber and a proprietary flame retardant package. It provides superb ignition resistance, rigidity, dimension stability and heat resistance. Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 3650 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 65.5 | MPa | |
| Break, 3.20 mm, Injection Molded | 62.7 | MPa | |
| Tensile Elongation (Break, 3.20 mm, Injection Molded) | 4.0 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 3790 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 109 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm, Injection Molded) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed | 149 | °C | |
| 1.8 MPa, Unannealed | 141 | °C | |
| 1.8 MPa, Annealed | 135 | °C | |
| Vicat Softening Temperature | 160 | °C | ASTM D1525 1 |
| Ball Indentation Temperature | > 125 | °C | IEC 60335-1 |
| CLTE - Flow (-40 to 80°C) | 3.8E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 110 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 2 | UL 94 | ||
| 1.59 mm | V-0 | ||
| 3.20 mm | 5VA | ||
| Oxygen Index 3 | 38 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 82.2 to 116 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoPet 3500 | TechnoCompound GmbH | PET | TechnoPet |
| VESTAMID® L LX9102 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| Alpha PVC 2235RSM-100 CLEAR 000X | AlphaGary | PVC, Semi-Rigid | Alpha PVC |
| Hostalen GD 9550 F | LyondellBasell Industries | HDPE | Hostalen |
| Hyundai EP PA66 LD380 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |