SAXALAC™ 120T
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9NhOA2_SAXALAC-120T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Saxalac 120T is an antistatic, easy flowing ABS injection molding grade, characterized by high impact strength, high stiffness and good resistance to heat distortion. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Moisture Content 1 | < 0.20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 7.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 22 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 65 | kJ/m² | |
| 23°C | 100 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 27 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180 | ||
| -30°C | 70 | kJ/m² | |
| 23°C | 100 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2(1.8 MPa, Unannealed, 60.0 mm Span) | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 102 | °C | ISO 306/B50 |
| Ball Pressure Test (95°C, 2.00 mm) | Pass | IEC 60335-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm, ALL) | HB | UL 94 | |
| Glow Wire Flammability Index | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | B130 |
| 2 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F200A (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Miramid® H3CF | BASF Leuna GmbH | Nylon 6 | Miramid® |
| U-polymer UM-8430RG | UNITIKA Plastics Division | Polyarylate | U-polymer |
| BioCeres® BC-LBI02 | FuturaMat | Biodeg Polymers | BioCeres® |
| GAPEX® RPP10EB19AL | Ferro Corporation | PP Homopolymer | GAPEX® |