Order Products : sales@su-jiao.com
LNP™ LUBRICOMP™ WL004 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9NZi4b_LNP-LUBRICOMP-WL004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* WL004 is a compound based on PBT resin containing 20% PTFE. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound WL-4040 Product reorder name: WL004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 2.1 to 2.4 | % | ASTM D955 |
| Across Flow : 24 hr | 2.1 to 2.4 | % | ASTM D955 |
| Across Flow : 24 hr | 2.1 to 2.3 | % | ISO 294-4 |
| Flow : 24 hr | 2.4 to 2.5 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.051 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2410 | MPa | ASTM D638 |
| -- | 2450 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 49.0 | MPa | ASTM D638 |
| Break | 45.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 9.8 | % | ASTM D638 |
| Break | 8.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2410 | MPa | ASTM D790 |
| -- | 2390 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 78.7 | MPa | ASTM D790 |
| -- | 77.1 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.33 | ||
| vs. Itself - Static | 0.24 | ||
| Wear Factor - Washer | 58.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 2 | 3.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 440 | J/m | ASTM D4812 |
| 23°C 3 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 0.960 | J | ASTM D3763 |
| -- | 0.500 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 55.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 61.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 9.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unilex™ UP 9035-I | United Polychem | PP Impact Copolymer | Unilex™ |
| Chemlon® 235-10 GM | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Dryflex® 500850 | ELASTO | TPE | Dryflex® |
| Petrothene® GA574189X02 | LyondellBasell Industries | LLDPE | Petrothene® |
| Shida 033 | JINJIANG City SHIDA Plastic Fine Co., Ltd. | SBS | Shida |