Order Products : sales@su-jiao.com
PRL PC/TP-GP3
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9MvFR9_PRL-PC-TP-GP3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PC/TP-GP3 is a Polycarbonate + Polyester (PC+Polyester) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 6.0 to 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 1.3 to 1.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 46.2 | MPa | |
| Break, 3.18 mm | 44.1 | MPa | |
| Flexural Modulus (3.18 mm) | 1790 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 66.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 480 | J/m | |
| 23°C, 3.18 mm | 800 | J/m | |
| Gardner Impact (3.18 mm) | > 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 116 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 76.7 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 227 to 243 | °C | |
| Middle Temperature | 232 to 249 | °C | |
| Front Temperature | 238 to 260 | °C | |
| Processing (Melt) Temp | 238 to 260 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8215-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Vi-Chem PVC VSR50D-80E | Vi-Chem Corporation | PVC, Rigid | Vi-Chem PVC |
| ICORENE® 1060 Enhanced Surface Finish | ICO Polymers EMEA, A Division of A. Schulman | LLDPE | ICORENE® |
| LNP™ THERMOCOMP™ PF008 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| Polifor® 6000/V0-AF-EP NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |