Fortron® 4332L6
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9MaOOE_Fortron-4332L6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fortron 4332L6 is a glass fiber/mineral filled injection molding grade, which is intended for applications requiring improved tensile and flexural properties, when compared to other GF/MIN reinforced PPS grades. The recommended processing parameters are similar to the standard grades. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.95 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.30 to 0.70 | % | |
| Flow | 0.20 to 0.60 | % | |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 21500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 160 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.2 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 21000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 270 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 220 | °C | ISO 75-2/C |
| CLTE | ISO 11359-2 | ||
| Flow | 1.4E-5 | cm/cm/°C | |
| Transverse | 3.1E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 320 to 340 | °C | |
| Mold Temperature | 140 | °C | |
| Screw L/D Ratio | 15.0:1.0 to 25.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE M300054 | SABIC Americas, Inc. | HDPE | SABIC® HDPE |
| Salflex 620TC | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| Geon™ Vinyl Dry Blend E7000 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Dry Blend |
| MAJORIS FT303 - 1451 | AD majoris | PP, Unspecified | MAJORIS |
| Petro Rabigh PP AZ564G | Rabigh Refining & Petrochemical Co. | PP Impact Copolymer | Petro Rabigh PP |