LNP™ STAT-KON™ MFD03 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9M5Xv7_LNPSTATKONMFD03compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON MFD03 is a compound based on Polypropylene resin containing 15% Glass Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound STATKON-MF-15 Product reorder name: MFD03 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.50 - 1.0 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 60.0 | MPa | ISO 527-2/5 |
| Fracture | 59.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 2.4 | % | ISO 527-2/5 |
| Fracture | 2.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4100 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 88.0 | MPa | ISO 178 |
| -- 4 | 50.0 | MPa | ISO 178 |
| Flexural Strain at Break 5 | 3.7 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, unannealed, 64.0mm span | 154 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 127 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 - 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 - 204 | °C | |
| Middle Temperature | 216 - 227 | °C | |
| Front Temperature | 238 - 249 | °C | |
| Processing (Melt) Temp | 227 - 249 | °C | |
| Mold Temperature | 32.2 - 48.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 2 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 B TFE 13 SI 2 | RTP Company | Nylon 610 | RTP |
| Skyrol® SH96D | SKC Inc. | PET | Skyrol® |
| TAIRIPRO K8003 | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| VINIKA® CB55EB | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Geon™ Vinyl Rigid Molding M3880 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |