Vibrathane® 6060
| Category: | PUR-Capro/TDI , Polyurethane (Polycaprolactone, TDI) |
| Manufacturer: | Chemtura |
| Trademark: | Vibrathane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9LU7cM_Vibrathane-6060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
VIBRATHANE 6060 is a polycaprolactone based TDI terminated liquid urethane prepolymer that is readily processable by conventional hand and machine mixing techniques. When cured with 4,4'-methylene-bis(2-chloroaniline), this member of the VIBRATHANE family produces high quality vulcanizates in the 60 Shore A hardness range. These tough, high resilience elastomers are characterized by:
This unusual prepolymer yields a high performance 60A elastomer when cured with MBCA, thereby avoiding the need for mixed curatives or plasticizers which are usually required to achieve hardnesses in this range. VIBRATHANE 6060 is a high quality product designed for use in high wear mining applications. Its long pot life and low viscosity are attributes that facilitate the casting of large as well as small fabricated parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% Strain | 0.276 | MPa | |
| 10% Strain | 0.552 | MPa | |
| 15% Strain | 0.896 | MPa | |
| 20% Strain | 1.24 | MPa | |
| 25% Strain | 1.65 | MPa | |
| Taber Abrasion Resistance (1000 Cycles, 100 g, H-18 Wheel) | 23.9 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 2.07 | MPa | |
| 300% Strain | 3.45 | MPa | |
| Tensile Strength | 30.3 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 480 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 33.3 | kN/m | ASTM D624 |
| Split | 3.9 | kN/m | ASTM D470 |
| Compression Set (70°C, 22 hr) | 6.0 | % | ASTM D395B |
| Bayshore Resilience | 30 | % | ASTM D2632 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -57.0 | °C | ASTM D746 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 10 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Pot Life | 9.0 | min | |
| Post Cure Time (115°C) | 16 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time (115°C) | 1.0 | hr |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PEI 6G/3L1 | Witcom Engineering Plastics B.V. | PEI | Witcom PEI |
| APEX® 71-2401-B | Teknor Apex Company | PVC, Flexible | APEX® |
| Elvax® 250 | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| InnoPlus HD1600J | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |
| Durethan® DP 2802/30 000000 | LANXESS Corporation | Nylon 66 | Durethan® |