RTP 201 TFE 13 SI 2 Datasheet,Nylon 66,RTP Company-SHANGHAI SUSHENG

Message
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 10% filler by weight
Additive	PTFE lubricant (13%) Silicone lubricant (2%)
Features	Lubrication
RoHS Compliance	Contact manufacturer
Appearance	Black Natural color
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.29	g/cm³	ASTM D792
Molding Shrinkage - Flow (3.18 mm)	0.70	%	ASTM D955
Water Absorption (23°C, 24 hr)	0.85	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	120		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	4480	MPa	ASTM D638
Tensile Strength	96.5	MPa	ASTM D638
Tensile Elongation (Break)	3.5	%	ASTM D638
Flexural Modulus	4140	MPa	ASTM D790
Flexural Strength	138	MPa	ASTM D790
Compressive Strength	89.6	MPa	ASTM D695
Coefficient of Friction			ASTM D1894
With Metal-Dynamic	0.12		ASTM D1894
With metal-static	0.10		ASTM D1894

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.18 mm)	43	J/m	ASTM D256
Unnotched Izod Impact (3.18 mm)	430	J/m	ASTM D4812

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, not annealed	249	°C	ASTM D648
1.8 MPa, not annealed	238	°C	ASTM D648

Flammability	Nominal Value		Test Method
Flame Rating (1.59 mm)	HB		UL 94

Additional Information
The value listed as Flammability, UL 94, was tested in accordance with RTP test standards.Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 12mil/in.Tensile Elongation, ASTM D-638: 3-4%Wear Factor, K, ASTM D-3702: 20E-10in³/min/ft/lb/hrCoefficient of Friction, Static, ASTM D-3702: 0.10Coefficient of Friction, Dynamic, ASTM D-3702: 0.12The wear factor and dynamic coefficient of friction were both tested on a Falex Model No.6 Wear Testing Machine at 50 FPM, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness.

Additional Information

The value listed as Flammability, UL 94, was tested in accordance with RTP test standards.Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 12mil/in.Tensile Elongation, ASTM D-638: 3-4%Wear Factor, K, ASTM D-3702: 20E-10in³/min/ft/lb/hrCoefficient of Friction, Static, ASTM D-3702: 0.10Coefficient of Friction, Dynamic, ASTM D-3702: 0.12The wear factor and dynamic coefficient of friction were both tested on a Falex Model No.6 Wear Testing Machine at 50 FPM, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness.

Injection	Nominal Value	Unit
Drying Temperature	79.4	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.20	%
Suggested Max Regrind	20	%
Rear Temperature	274 - 288	°C
Middle Temperature	274 - 288	°C
Front Temperature	274 - 288	°C
Mold Temperature	65.6 - 107	°C
Injection Pressure	82.7 - 138	MPa

Category:	Nylon 66 , Polyamide 66
Manufacturer:	RTP Company
Trademark:	RTP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	9LIcDS_RTP-201-TFE-13-SI-2.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Ronalen M40	Roonamid a.s.	PP, Unspecified	Ronalen
Cosmic Alkyd 3D36	Cosmic Plastics, Inc.	Alkyd	Cosmic Alkyd
Generic PC Alloy - Glass Fiber	Generic	PC Alloy	Generic
KIBILAC® PW-978B	CHI MEI CORPORATION	ASA	KIBILAC®
LITEN FB 75	UNIPETROL RPA	HDPE, HMW	LITEN