Abstron IPM 2000
| Category: | ABS+Acrylic , Acrylonitrile Butadiene Styrene + Acrylic (PMMA) |
| Manufacturer: | Bhansali Engineering Polymers Limited |
| Trademark: | Abstron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9L9k28_Abstron-IPM-2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Abstron IPM 2000 is an Acrylonitrile Butadiene Styrene + Acrylic (PMMA) (ABS+Acrylic) product. It is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, Injection Molded) | 110 | ASTM D785 | |
| Pencil Hardness 1 | HB | ASTM D3363 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, 3.20 mm, Injection Molded) | 51.0 | MPa | ASTM D638 |
| Flexural Modulus 3(6.40 mm, Injection Molded) | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm, Injection Molded) | 65.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm, Injection Molded | 150 | J/m | |
| 23°C, 6.40 mm, Injection Molded | 120 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(1.8 MPa, Annealed, 6.40 mm, Injection Molded) | 92.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 45°, 7.5 N |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | Annealed at 85°C for 2 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN SEP-550H | Lotte Chemical Corporation | PP Random Copolymer | RANPELEN |
| TOTAL Polystyrene Crystal 1340 | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| DILAMID® 6 FV 15 NATURAL | Dilaplast S.p.A. | Nylon 6 | DILAMID® |
| Karina STRAW PVC COMPOUND 837-38/ 29-E-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Evoprene™ 087 | Mexichem Specialty Compounds Inc. | TPE | Evoprene™ |