ULTEM™ 2410R resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9L7sK5_ULTEM2410Rresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.61 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 5.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 - 0.30 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.13 | % | ASTM D570 |
| Equilibrium, 23°C | 0.90 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 11700 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 179 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 11700 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 100 mm Span) | 241 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 430 | J/m | ASTM D4812 |
| Reverse Notch Izod Impact (3.20 mm) | 480 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 216 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 213 | °C | ASTM D648 |
| Vicat Softening Temperature | 234 | °C | ASTM D1525 6 |
| CLTE - Flow (-20 to 150°C) | 1.4E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 170 | °C | UL 746 |
| RTI Imp | 170 | °C | UL 746 |
| RTI | 170 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.5E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm, in Oil) | 24 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.70 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 2.0E-3 | ASTM D150 | |
| Arc Resistance 7 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 5 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.254 mm | V-0 | UL 94 | |
| 1.47 mm | 5VA | UL 94 | |
| Oxygen Index | 54 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 332 - 399 | °C | |
| Middle Temperature | 338 - 399 | °C | |
| Front Temperature | 343 - 399 | °C | |
| Nozzle Temperature | 343 - 399 | °C | |
| Processing (Melt) Temp | 349 - 399 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| 7 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1402 L | RTP Company | PESU | RTP |
| Viprene™ G55A-32U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| Hifax CB 131 G | LyondellBasell Industries | PP, Unspecified | Hifax |
| Karina LILAC PVC COMPOUND 830-34/148-IS-RG-PO (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLUSTEK PA303G33 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |